hpb89-2 化学元素 成分含量(%)
成分 fe ni cu pb zn
最 小值 - - 87.5 1.3 5
最 大 值 0.1 0.7 90.5 2.5 11.2
gb hpb89-2 gb/t 5231 mechanical
yield tensile impact elongation reduction in cross section on fracture as-heat-treated condition brinell hardness (hbw)
rp0.2 (mpa) rm (mpa) kv/ku (j) a (%) z (%)
457 (≥) 611 (≥) 32 31 34 solution***aging, annealing, ausaging, q+t,etc 133
gb hpb89-2 gb/t 5231 physical
physical properties of gb hpb89-2 gb/t 5231 are mainly indicated by modulus of electrical resistance value, thermal conductivity, specific thermal capacity, coefficient of thermal expansion, elasticity, poisson's ratio, density, etc.
temperature modulus of elasticity mean coefficient of thermal expansion 10-6/(°c) between 20(°c) and thermal conductivity specific thermal capacity specific electrical resistivity density poisson’s coefficient, ν
(°c) (gpa) (w/m·°c) (j/kg·°c) (ω mm2/m) (kg/dm3)
22 - - 0.31 -
324 227 - 23.3 413 -
426 - 13 23.2 122 124