zhpbd59-1铸造铅黄铜棒
gb zhpbd59-1 gb 8737 introduction
用途:铸造黄铜锭。
热处理:1469°c-1367°c。
gb zhpbd59-1 gb 8737 chemical
gb zhpb d59-1 gb 8737是由什么制成的?gb zhpb d59-1 gb 8737元素 含量,gb zhpb d59-1 gb 8737成分,gb zhpb d59-1 gb8737铸件分析
element min max similar
zn - - -
sb - 0.05 -
pb 0.8 1.9 -
p - 0.01 -
fe - 0.6 -
cu 57 61 -
al - 0.2 -
gb zhpbd59-1 gb 8737 mechanical
yield tensile impact elongation reduction in cross section on fracture as-heat-treated condition brinell hardness (hbw)
rp0.2 (mpa) rm (mpa) kv/ku (j) a (%) z (%)
935 (≥) 989 (≥) 32 21 32 solution***aging, annealing, ausaging, q+t,etc 433
gb zhpbd59-1 gb 8737 physical
gb zhpb d59-1 gb 8737的物理性能主要包括弹性模量、热膨胀系数、导热系数、比热容、电阻值、密度、泊松比等。
temperature modulus of elasticity mean coefficient of thermal expansion 10-6/(°c) between 20(°c) and thermal conductivity specific thermal capacity specific electrical resistivity density poisson’s coefficient, ν
(°c) (gpa) (w/m·°c) (j/kg·°c) (ω mm2/m) (kg/dm3)
11 - - 0.21 -
324 764 - 33.3 334 -
348 - 41 24.2 421 212
gb zhpbd59-1 gb 8737 processing service
zhpbd59-1铸造铅黄铜棒是一种广泛应用于阀门、管道、泵、工具等领域的重要材料。它具有优良的切削加工性能和耐磨性,能够满足各种复杂零件的制造要求。
zhpbd59-1铸造铅黄铜棒的化学成分主要由铜、铅、铁等元素 组成,其中铜元素 的含量较高,保证了材料具有良好的强度和耐腐蚀性能。铅元素 的加入使得材料具有更好的润滑性和耐磨性,能够有效地提高零件的使用寿命。此外,zhpbd59-1铸造铅黄铜棒还含有适量的铁元素 ,保证了材料的硬度和强度。
在制造过程中,zhpbd59-1铸造铅黄铜棒需要通过精密的铸造工艺来保证其内部组织和性能的稳定性。同时,为了确保其切削加工性能和耐磨性,需要进行特殊的热处理和表面处理。