cuzn39pb2al压铸件用黄铜
uni cuzn39pb2aluni en 1982 chemical
uni cc766s uni en 1982数据表和uni cc766s uni en 82化学成分见下表。
element min max similar
zn - - -
sn - 0.5 -
si - 0.6 -
sb - 0.1 -
pb - 0.5 -
ni - 2 -
mn - 0.5 -
fe - 0.5 -
cu 60 64 -
al 0.3 1.8 -
uni cuzn39pb2al uni en 1982 mechanical
yield tensile impact elongation reduction in cross section on fracture as-heat-treated condition brinell hardness (hbw)
rp0.2 (mpa) rm (mpa) kv/ku (j) a (%) z (%)
959 (≥) 571 (≥) 34 13 32 solution***aging, annealing, ausaging, q+t,etc 122
uni cuzn39pb2al uni en 1982 physical
uni cuzn39pb2al uni en 1982钢的物理性能包括高质量、低重量、坚固性、延展性和抗侵蚀性。
temperature modulus of elasticity mean coefficient of thermal expansion 10-6/(°c) between 20(°c) and thermal conductivity specific thermal capacity specific electrical resistivity density poisson’s coefficient, ν
(°c) (gpa) (w/m·°c) (j/kg·°c) (ω mm2/m) (kg/dm3)
34 - - 0.12 -
987 735 - 13.3 432 -
514 - 42 32.2 444 313
uni cuzn39pb2al uni en 1982 processing service
cuzn39pb2al压铸件是一种以黄铜为主要成分的合金材料。这种合金具有优良的铸造性能、机械性能和耐腐蚀性能,因此在许多领域得到广泛应用。
在cuzn39pb2al压铸件中,黄铜的含量较高,保证了其具有良好的铸造性能和机械性能。这种合金的塑性和韧性较高,可以进行深拉伸和弯曲等加工操作,同时其强度和硬度也得到了保证。此外,cuzn39pb2al压铸件还具有优良的耐腐蚀性能,可以在各种环境下长期稳定工作。
由于cuzn39pb2al压铸件具有以上优点,因此被广泛应用于汽车、电子、通讯、机械制造等领域。例如,它可以用于制造汽车上的进气管、冷凝器、散热器等零部件,也可以用于制造电子产品的外壳、螺母、螺栓等零部件。