cw624n,加工铅黄铜棒
1. cw624n的化学成分
according to din en 13388 (in ％ of mass)
cu zn pb ni fe sn al comment other elements
55,0- rest 1,6- 0,30 0,30 0,30 0,05- - 0,20
57,0 3,0 0,5
2. cw624n的力学性能
根据din en 12167型材/棒材（通用条件）
condition nominal thickness tensile strength yield strength ultimate elongation rigor
in mm rm in mpa rp0,2 in mpa in ％ (min.) hbs
over up to min max min max a50 a
a100
m all as manufactured - without specification of mechanical values
physical properties general properties
(guide values for 20° c)
density of g/cm3 8,4 resistance to:
solidification range ° c 870-885 - organic materials 2
electrical conductivity ms/m 16,4 - neutral / alkaline compounds 2
thermal conductivity w/(mk) 126 formability
therm. linear expansion- - warm 1
coeffizient 10-6/k 21,2 - cold 5
modulus of elasticity n/mm2 97
connection works surface treatment
- gas-shielded welding 5 mechanical polishing 2
- gas welding 5 electrolytic polishing 5
- resistance welding (blunt) 5 electroplating 1
- hard soldering 3
- soft soldering 1
machinability
generally 2
cw624n是一种加工铅黄铜棒,具有优异的机械性能和耐腐蚀性。它广泛应用于各种机械零件的制造,如螺栓、螺母、轴套等。由于其优良的切削性能和耐磨性,cw624n也常被用于制造各种工具和刀具。
cw624n的化学成分包括铜、铅、锌等元素 ,其中铜是主要成分。铅的加入使得cw624n具有更好的切削性能和耐磨性,而锌则提高了其耐腐蚀性和强度。这些元素 的合理配比使得cw624n具有优异的综合性能。
在制造过程中,cw624n经过了热轧、冷轧、拉拔等工艺处理,使其组织更加致密,力学性能更加优异。同时,为了满足不同客户的需求,cw624n还具有多种规格和尺寸可供选择。
此外,cw624n还具有良好的焊接性能和可加工性,可以方便地进行切割、钻孔、车削等加工操作。同时,它也具有较好的耐腐蚀性,可以在各种恶劣环境下长期使用。
总之,cw624n是一种优质的加工铅黄铜棒,具有优异的机械性能、耐腐蚀性和切削性能。它广泛应用于各种机械零件的制造和工具刀具的制造,是一种非常受欢迎的金属材料。